Stability of growing polymer chain ends for nitroxide-mediated photo-living radical polymerization

The stability of the growing polymer chain ends for the nitroxide-mediated photo-living radical polymerization of methyl methacrylate (MMA) was explored through block copolymerization with isopropyl methacrylate ( ⁱ PMA). The block copolymerization of ⁱ PMA was performed with the PMMA prepolymer prepared by the photopolymerization of MMA using the racemic-(2RS,2′RS)-azobis(4-methoxy-2,4-dimethylvaleronitrile) (r-AMDV) as the initiator, 4-methoxy-2,2,6,6-tetramethylpiperidine-1-oxyl (MTEMPO) as the mediator, and (4-tert-butylphenyl)-diphenylsulfonium triflate ( ^t BuS) as the photo-acid generator. When the polymerization of MMA was carried out for 6.5 h, the resulting block copolymer showed a bimodal GPC due to the deactivation of part of the growing chain ends of the prepolymer. On the other hand, when the MMA polymerization was shortened to 5 h, the unimodal block copolymer was obtained without deactivation of the prepolymer.