| Abstract: | The synthesis of low‐molecular‐weight (weight‐average molecular weight < 45,000 g/mol) lactic acid polymers through the dehydropolycondensation of L ‐lactic acid was investigated. Polymerizations were carried out in solution with solvents (xylene, mesitylene, and decalin), without a solvent using different Lewis acid catalysts (tetraphenyl tin and tetra‐n‐butyldichlorodistannoxane), and at three different polymerization temperatures (143, 165, and 190 °C). The products were characterized with differential scanning calorimetry, size exclusion chromatography, vapor pressure osmometry, 13C NMR, and matrix‐assisted laser desorption/ionization time‐of‐flight (MALDI‐TOF). The resulting polymers contained less than 1 mol % lactide, as shown by NMR. The number‐average molecular weights were calculated from the ratio of the area peaks of ester carbonyl and carboxylic acid end groups via 13C NMR. The stereosequences were analyzed by 13C NMR spectroscopy on the basis of triad effects. Tetraphenyl tin was an effective transesterification catalyst, and the randomization of the stereosequence at 190 °C was observed. In contrast, the distannoxane catalyst caused comparatively less transesterification reaction, and the randomization of the stereosequences was slow even at 190 °C. The L ‐lactic acid and D ‐lactic acid isomers were added to the polymer chain in a small, blocky fashion. The MALDI‐TOF spectra of poly(L ‐lactic acid) (PLA) chains doped with Na+ and K+ cations showed that the PLA chains had the expected end groups. The MALDI‐TOF analysis also enabled the simultaneous detection of the cyclic oligomers of PLA present in these samples, and this led to the full structural characterization of the molecular species in PLA. © 2005 Wiley Periodicals, Inc. J Polym Sci Part A: Polym Chem 43: 2164–2177, 2005 |