Thermal stability and reactivity in oxygen of potassium ferrites with spinel structure |
| |
| Authors: | B. Gillot M. Laarj B. Maachi A. Rousset |
| |
| Affiliation: | (1) Laboratoire de Recherches sur la Réactivité des Solides. U. A. 23 CNRS, Université de Bourgogne, Faculté des Sciences Mirande, B. B. 138, F-21004 Dijon, France;(2) Laboratoire de Chimie des Matériaux Inorganiques, Loe-CNRS, Université Paul Sabatier, 29, Rue Jeanne Marvig, B. P. 4347, F-31055 Toulouse Cedex, France |
| |
| Abstract: | The potassium content really incorporated in the spinel lattice of the magnetite determined by thermogravimetric analysis in vacuum or in oxygen was about 2.45 wt%. In spite of this low content, the potassium strongly stabilises the defect spinel structure resulted by the potassium-substituted magnetite oxidation and increases the transformation temperature of the defect phases into  -Fe2O3 or KFe11O17.
Zusammenfassung Der tatsächlich in das Spinellgitter von Magnetit eingebaute Kaliumgehalt beträgt 2.45 Gewichtsprozente. Dies wurde durch TG-Analyse in Vakuum bzw. Sauerstoff ermittelt. Trotz dieses geringen Gehaltes wird das defekte Spinell des durch Oxydation erhaltenen kaliumsubstituierten Magnetits durch Kalium stark stabilisiert, was ein Ansteigen der Temperatur für die Umwandlung der defekten Phase in Fe2O3 oder KFe11O17 nach sich zieht. |
| |
| Keywords: | |
| 本文献已被 SpringerLink 等数据库收录！ |
|