| Abstract: | Several masked isocyanates were prepared with variations in both the type of isocyanate and masking group. They were characterized by elemental analysis and NMR spectroscopy, and their unblocking temperatures were determined. In general, higher unblocking temperatures were obtained using acyclic and cyclic aliphatic isocyanates and fluorinated phenols. Those with unblocking temperatures in the range of 120–180°C were incorporated into MY 720/DDS epoxy resin prior to cure. Highly fluorinated variations were incompatible with the resin. IR and DSC analyses showed that residual functional groups in the epoxy resin reacted with the masked isocyanates. Reductions in moisture absorption as high as 65% were obtained depending on the masked isocyanate. DMA studies showed that the Tg of the epoxy resin is lowered by incorporation of the masked isocyanate but the elastic modulus (E′) is relatively unchanged at temperatures below Tg. |