Chemical synthesis of spinel nickel ferrite (NiFe2O4) nano-sheets

The present investigation is related to the deposition of single-phase nano-sheets spinel nickel ferrite (NiFe₂O₄) thin films onto glass substrates using a chemical method. Nano-sheets nickel ferrite films were deposited from an alkaline bath containing Ni²⁺ and Fe²⁺ ions. The films were characterized for their structural, surface morphological and electrical properties by means of X-ray diffraction (XRD), transmission electron microscope (TEM), Fourier transform infrared spectroscopy (FT-IR), scanning electron microscopy (SEM), and two-point probe electrical resistivity techniques. The X-ray diffraction pattern showed that NiFe₂O₄ nano-sheets are oriented along (3 1 1) plane. The FT-IR spectra of NiFe₂O₄ films showed strong absorption peaks around 600 and 400 cm⁻¹ which are typical for cubic spinel crystal structure. Microstructural study of NiFe₂O₄ film revealed nano-sheet like morphology with average sheet thickness of 30 nm. The room temperature electrical resistivity of the NiFe₂O₄ nano-sheets was 10⁷ Ω cm.