Corrosion behavior of Nd9.4Pr0.6Febal.Co6B6Ga0.5TixCx (x=0, 1.5, 3, 6) nanocomposites annealed melt-spun ribbons |
| |
Authors: | M. Nezakat A. Amadeh T. Ohkubo |
| |
Affiliation: | a School of Metallurgy and Materials Engineering, Faculty of Engineering, University of Tehran, Tehran 11155-4563, Iran b Iranian Research Organization for Science and Technology (IROST), Tehran 15815-3538, Iran c National Institute for Materials Science, 1-2-1 Sengen, Tsukuba 305-0047, Japan |
| |
Abstract: | The effect of Ti and C additions on the corrosion behavior of Nd9.4Pr0.6Febal.Co6B6Ga0.5TixCx (x=0, 1.5, 3, 6) isotropic nanocomposite melt-spun ribbons in 3.5 wt% sodium chloride solution was studied. The melt-spun ribbons were annealed at 750 °C for 10 min in argon-filled quartz capsules. The microstructure of multiphase nanocrystalline samples and corrosion products was characterized using the X-ray diffraction and electron microscopy techniques. The electrochemical behavior was assessed using potentiodynamic polarization and electrochemical impedance spectroscopy. The results show that the addition of Ti and C increases the corrosion resistance of NdFeB ribbons; the best corrosion resistance was obtained for 1.5 wt% Ti and C content. |
| |
Keywords: | NdFeB nanocomposite Corrosion behavior Effect of Ti and C Electrochemical measurement |
本文献已被 ScienceDirect 等数据库收录! |
|