Synthesis and properties of hyperbranched polybenzimidazoles via A2 + B3 approach
Authors:Hongjie Xu  Kangcheng Chen  Xiaoxia Guo  Jianhua Fang  Jie Yin
Institution:1. School of Chemistry and Chemical Technology, Shanghai Jiao Tong University, 800 Dongchuan Road, Shanghai 200240, China;2. College of Chemistry and Materials Science, Fujian Normal University, 8 Shangsan Road, Fuzhou 350007, China;3. School of Chemistry and Chemical Technology, Shanghai Jiao Tong University, 800 Dongchuan Road, Shanghai 200240, ChinaSchool of Chemistry and Chemical Technology, Shanghai Jiao Tong University, 800 Dongchuan Road, Shanghai 200240, China
Abstract:Hyperbranched polybenzimidazoles (HBPBIs) were successfully synthesized by condensation polymerization of 1,3,5‐benzenetricarboxylic acid (BTA) and 3,3′‐diaminobenzidine (DAB) in polyphosphoric acid (PPA) at 190 °C. Different monomer addition manners and molar ratios resulted in different polymers, that is, simultaneous addition of BTA and DAB with the molar ratio of 1:1 (manner 1) gave carboxyl‐terminated HBPBI (HBPBI‐1), whereas the addition of BTA portion‐wise to DAB solution in PPA with the molar ratio of DAB:BTA = 2:1 (manner 2) yielded amine‐terminated HBPBI (HBPBI‐2). The free carboxyl and amino groups of HBPBI‐1 and HBPBI‐2 could further react with o‐diaminobenzene and benzoic acid, respectively, to form the chemically modified polymers. Except HBPBI‐2, all the HBPBIs showed good solubility in some organic solvents (e.g., dimethyl sulfoxide and N,N‐dimethylacetamide). Thermogravimetric analysis measurement revealed that HBPBIs except HBPBI‐1 had high thermal stability (>450 °C). HBPBI membranes with good mechanical properties were obtained by crosslinking treatment of partially chemically modified HBPBIs with terephthaldehyde (TPA) during the film cast process. The HBPBI membranes had high phosphoric acid uptake and the phosphoric acid‐doped HBPBI‐6 (40% o‐diamino groups were reacted with benzoic acid) membrane showed higher tensile strength than the acid‐doped commercial PBI despite the higher doping level of the former. © 2006 Wiley Periodicals, Inc. J Polym Sci Part A: Polym Chem 45: 1150–1158, 2007
Keywords:doping  hyperbranched polybenzimidazoles  mechanical properties  membrane  synthesis
设为首页 | 免责声明 | 关于勤云 | 加入收藏

Copyright©北京勤云科技发展有限公司  京ICP备09084417号