Sulfonated poly(fluorenyl ether) membranes containing perfluorocyclobutane groups for fuel cell applications

This paper describes the preparation and electrochemical properties of new proton conducting polymer membranes, sulfonated poly(fluorenyl ether) membrane-containing perfluorocyclobutane (PFCB) moieties for fuel cell applications. The sulfonated polymers were prepared via thermal cyclodimerization of 9,9-bis(4-trifluorovinyloxyphenyl)fluorene and subsequent post-sulfonation using chlorosulfonic acid (CSA) as a sulfonating agent. The post-sulfonation reaction was carried out by changing the molar ratio of CSA/repeating unit of the polymer at room temperature for 5 h and the resulting sulfonated polymers showed different degrees of sulfonation (DS) and ion exchange capacities (IEC). With the increment of CSA content, the DS, IEC and water uptake of the sulfonated polymer membranes increased. Their proton conductivity was investigated as a function of temperature. The polymer membrane with an IEC value of 1.86 mmol/g showed a water content of 25% similar to Nafion-115's but showed higher proton conductivity than Nafion-115 over the temperature 25–80 °C. The polymer membrane with lower water uptake and higher IEC showed similar proton conductivity and methanol permeability to Nafion-115. These results confirmed that the sulfonated poly(fluorenyl ether)-containing PFCB groups could be a promising material for fuel cell membranes.