Blends of normal high density and ultra-high molecular weight polyethylene, γ irradiated at a low dose

The kinetics of a nonisothermal crystallization and melting of irradiated with dose of 6 Mrad blends of an ultra-high molecular-weight polyethylene (UHMWPE) and a high-density polyethylene with normal molecular weight (NMWPE) is investigated by means of DSC. The blends have been prepared at temperature below the flow temperature of UHMWPE: The enthalpies of melting of the polyethylenes increase, while those of their blends decrease after irradiation. The enthalpies of crystallization of the pure polyethylenes are higher, while those of their blends almost do not change or are a bit higher after irradiation. The rates of a nonisothermal crystallization and melting of the polyethylenes increase, while those of the polyethylenes in the blends decrease after irradiation. Thermomechanical measurements under constant load in wide-temperature interval of irradiated polyethylenes and their blends have been made. A high-elastic plateau in viscous-liquid state is established on the thermomechanical curves of UHMWPE, and the blends with high content of UHMWPE. On the basis of results obtained assumptions have been made about the processes taking place in the blends under the action of irradiation, as well as about the character of the mutual influence between the components in the process of irradiation.