Thermosensitive Poly(N-isopropylacrylamide)-g -Polyamidoamine Dendrimer Derivatives: Preparation and the Drug Release Behaviors

Summary: A series of thermally responsive dendritic core-shell polymers were prepared based upon dendritic polyamidoamine (PAMAM), modified with carboxyl end-capped linear poly(N-isopropylacrylamide) (PNIPAAm-COOH) in different ratios via an esterification process to obtain PNIPAAm-g-PAMAM. The graft ratio of PNIPAAm could be adjusted by changing the feed ratio of PAMAM-OH to PNIPAAm-COOH and was verified by ¹H NMR and gel penetration chromatography (GPC). The lower critical solution temperature (LCST) of PNIPAAm-g-PAMAM evaluated by UV-vis spectrophotometer was about 32 °C. Indomethacin (IMC) as a model drug was loaded in the thermosensitive polymer-grafted dendrimer derivative and its release behavior was studied below and above its LCST (27 °C vs 37 °C). Results showed that the LCST of PNIPAAm-g-PAMAM was around 32 °C compared with that of the pure PNIPAAm. The release behavior of the indomethacin entrapped in the internal cavities of the PNIPAAm-g-PAMAM showed that almost 77% of the drug was cumulatively released at 27 °C after 10 hours, whereas only 20% was released at 37 °C. The release rate of IMC from the IMC/PNIPAAm-g-PAMAM complex at 37 °C is significantly slower than that at 27 °C, which indicates that the PNIPAAm chains grafted on the surface of PAMAM dendrimer could act as a channel switching on-off button through expending or contracting in response to the temperature variation and could control the drug release by varying the surrounding temperature.