Polymerization of pyromellitic dianhydride with 3,3′-diaminobenzidine in aprotic solvents I. Reaction variables

The solution polymerization of pyromellitic dianhydride with 3,3′-diaminobenzidine to form poly(amide acid amine) was investigated under a variety of reaction conditions. Polymer viscosity and gel formation were highly affected by changes in the order of monomer addition, the type of process (powder or solution), monomer concentration, monomer stoichiometry, and type of solvent. Minor effects were noted with changes in polymerization temperature and the presence of small amounts of water. A limiting intrinsic viscosity of 1.2–1.5 dl/g was observed, regardless of polymerization conditions. The polymerization had a strong tendency to gel at high concentrations and when monomer molar ratios approached 1:1. The conditions which retarded or promoted the formation of macrogel were well-defined, and macrogel but not microgel could be prevented. The polymerization was conducted successfully only in aprotic solvents. No imidazopyrrol-one units were detected in polymer made in polyphosphoric acid at elevated temperatures.