PREPARATION, CHARACTERIZATION AND ELECTROCHEMICAL PROPERTIES OF POLYPYRROLE-POLYSTYRENE SULFONIC ACID COMPOSITE FILM

Polypyrrole-polystyrene sulfonic acid (PPy-PSSA) composite films have been electrosynthesized in an aqueous solution of PSSA. The electro-active films exhibit cation exchange during the redox process. Infrared, Raman and energy-dispersive spectroscopic results demonstrated that the polyanion of PSS^- is co-deposited into the PPy matrix and couldn‘t be stripped from the film extensively by dedoping. The doping level together with dipolaron content of the PPy-PSSA composite film increases during electrochemical polymerization process. SEM images revealed that the composite film has smooth and compact morphology and AFM pictures suggested that PPy chains are possibly grown perpendicular to the electrode surface. TGA tests indicated that the composite films has much better thermal stability than that of pure PPy.Furthermore, electrochemical studies showed that the relaxation process at certain holding potential has great effect on the shape of the cyclic voltammetric curves of PPy-PSSA composite film. The composite film exhibits cation and anion exchange during the redox process after undergoing the relaxation step. It is more difficult for divalent anion to enter the polymer matrix than a univalent ion, and a large cation such as (CH3CH2CH2CH2)4N^ cannot be involved in the ion exchange process.

PREPARATION, CHARACTERIZATION AND ELECTROCHEMICAL PROPERTIES OF POLYPYRROLE-POLYSTYRENE SULFONIC ACID COMPOSITE FILM

Polypyrrole-polystyrene sulfonic acid (PPy-PSSA) composite films have been electrosynthesized in an aqueous solution of PSSA. The electro-active films exhibit cation exchange during the redox process. Infrared, Raman and energydispersive spectroscopic results demonstrated that the polyanion of PSS- is co-deposited into the PPy matrix and couldn't be stripped from the film extensively by dedoping. The doping level together with dipolaron content of the PPy-PSSA composite film increases during electrochemical polymerization process. SEM images revealed that the composite film has smooth and compact morphology and AFM pictures suggested that PPy chains are possibly grown perpendicular to the electrode surface. TGA tests indicated that the composite films has much better thermal stability than that of pure PPy.Furthermore, electrochemical studies showed that the relaxation process at certain holding potential has great effect on the shape of the cyclic voltammetric curves of PPy-PSSA composite film. The composite film exhibits cation and anion exchange during the redox process after undergoing the relaxation step. It is more difficult for divalent anion to enter the polymer matrix than a univalent ion, and a large cation such as (CH3CH2CH2CH2)4N cannot be involved in the ion exchange process.