Luminescence of Ce and Pr doped Sr2Mg(BO3)2 under VUV-UV and X-ray excitation

This report presents the luminescence properties of Ce³⁺ and Pr³⁺ activated Sr₂Mg(BO₃)₂ under VUV-UV and X-ray excitation. The five excitation bands of crystal field split 5d states are observed at about 46 729, 44 643, 41 667, 38 314 and 29 762 cm⁻¹ (i.e. 214, 224, 240, 261 and 336 nm) for Ce³⁺ in the host lattice. The doublet Ce³⁺ 5d→4f emission bands were found at about 25 840 and 24 096 cm⁻¹ (387 and 415 nm). The influence of doping concentration and temperature on the emission characteristics and the decay time of Ce³⁺ in Sr₂Mg(BO₃)₂ were investigated. For Pr³⁺ doped samples, the lowest 5d excitation band was observed at about 42017 cm⁻¹ (238 nm), a dominant band at around 35714 cm⁻¹ (280 nm) and two shoulder bands were seen in the emission spectra. The excitation and emission spectra of Ce³⁺ and Pr³⁺ were compared and discussed. The X-ray excited luminescence studies show that the light yields are ∼3200±230 and ∼1400±100 photons/MeV of absorbed X-ray energy for the samples Sr_1.86Ce_0.07Na_0.07Mg(BO₃)₂ and Sr_1.82Pr_0.09Na_0.09Mg(BO₃)₂ at RT, respectively.