Multiatomic step formation on GaAs(001) vicinal surfaces during thermal treatment

We observed the surface morphology of vicinal GaAs(001) after thermal treatment in AsH₃/H₂ atmosphere by atomic force microscopy (AFM). Clear multiatomic steps were formed under the high temperature thermal treatment. Next, we investigated the mechanism of step bunching during thermal treatment by two experiments from the view point of Ga atom evaporation. One is the selective thermal treatment using a partially masked GaAs wafer, and the evaporation amount of Ga atoms was estimated by AFM. The other is the investigation of photoluminescence (PL) peak energy shifts for AlGaAs/GaAs single quantum wells with a thermal treatment process at the top of the GaAs quantum well layer, compared to those without thermal treatment. These results indicate that the evaporation hardly occurs during the thermal treatment process. Therefore, step bunching phenomena on GaAs(001) vicinal surfaces during thermal treatment are probably caused by migration of the atoms detached from upside steps and their re-incorporation to downside steps.