Quaternäre Caesium‐Kupfer(I)‐Lanthanoid(III)‐Selenide vom Typ CsCu3M2Se5 (M = Sm,Gd — Lu)

Quaternary Cesium Copper(I) Lanthanoid(III) Selenides of the Type CsCu₃M₂Se₅ (M = Sm, Gd — Lu) By oxidation of mixtures of copper and lanthanoid metal with elemental selenium in molar ratios of 1 : 1 : 2 and in addition of CsCl quaternary cesium copper(I) lanthanoid(III) selenides with the formula CsCu₃M₂Se₅ (M = Sm, Gd — Lu) were obtained at 750 °C within a week from torch‐sealed evacuated silica tubes. An excess of CsCl as flux helps to crystallize golden yellow or red, needle‐shaped, water‐resistant single crystals. The crystal structure of CsCu₃M₂Se₅ (M = Sm, Gd — Lu) (orthorhombic, Cmcm, Z = 4; e. g. CsCu₃Sm₂Se₅: a = 417.84(3), b = 1470.91(8), c = 1764.78(9) pm and CsCu₃Lu₂Se₅: a = 407.63(3), b = 1464.86(8), c = 1707.21(9) pm, respectively) contains MSe₆]^9— octahedra which share edges to form double chains running along 100]. Those are further connected by vertices to generate a two‐dimensional layer parallel to (010). By edge‐ and vertex‐linking of CuSe₄]^7— tetrahedra two crystallographically different Cu⁺ cations build up two‐dimensional puckered layers parallel to (010) as well. These sheet‐like structure interconnects the equation/tex2gif-stack-3.gif{M₂Se₅]^4—} layers to create a three‐dimensional network according to equation/tex2gif-stack-4.gif{Cu₃M₂Se₅]^—}. Thus empty channels along 100] form, apt to take up the Cs⁺ cations. These are surrounded by eight plus one Se^2— anions in the shape of (2+1)‐fold capped trigonal prisms with Cs—Se distances between 348 and 368 pm (8×) and 437 (for M = Sm) or 440 pm (for M = Lu), respectively, for the ninth ligand.