Influence of V2O5 on the magnetic properties of nickel–zinc–copper ferrites

Additions of V₂O₅ were used to decrease the sintering temperature and to enhance the densification of NiZnCu ferrite. With a small amount of V₂O₅ (0.6–1.2 wt%) as a sintering aid, densification at low sintering temperature was observed. EDS analyses showed the presence of vanadium inside the ferrite grains. Microstructure investigation revealed heterogeneous grain size. Magnetic properties were deteriorated when increasing the V₂O₅ content. As a consequence, the permeability decreased and the core losses increased, which can be explained by the pinning of the domain walls to the grain defects.