The phase relations in the In2O3A2O3BO systems at elevated temperatures [A: Fe or Ga, B: Cu or Co]

The phase relations in the In₂O₃Fe₂O₃CuO system at 1000°C, the In₂O₃Ga₂O₃CuO system at 1000°C, the In₂O₃Fe₂O₃CoO system at 1300°C, and the In₂O₃Ga₂O₃CoO system at 1300°C were determined by means of a classical quenching method. InFeCuO₄ (a = 3.3743(4) Å, c = 24.841(5) Å), InGaCuO₄ (a = 3.3497(2) Å, c = 24.822(3) Å), and InGaCoO₄ (a = 3.3091(2) Å, c = 25.859(4) Å) having the YbFe₂O₄ crystal structure, In₂Fe₂CuO₇ (a = 3.3515(2) Å, c = 28.871(3) Å), In₂Ga₂CuO₇ (a = 3.3319(1) Å, c = 28.697(2) Å), and In₂FeGaCuO₇ (a = 3.3421(2) Å, c = 28.817(3) Å) having the Yb₂Fe₃O₇ crystal structure, and In₃Fe₃CuO₁₀ (a = 3.3432(3) Å, c = 61.806(6) Å) having the Yb₃Fe₄O₁₀ crystal structure were found as the stable ternary phases. There is a continuous series of solid solutions between InFeCoO₄ and Fe₂CoO₄ which have the spinel structure at 1300°C. The crystal chemical roles of Fe³⁺ and Ga³⁺ in the present ternary systems were qualitatively compared.