Self-limiting nature in atomic-layer epitaxy of rutile thin films from TiCl4 and H2O on sapphire (0 0 1) substrates

The atomic-layer epitaxy of rutile thin films on sapphire (0 0 1) substrates was studied in the controlled growth of titanium oxide films by sequential surface chemical reactions using sequentially fast pressurized titanium tetrachloride (TiCl₄) and water (H₂O) vapor pulses. Optical constants and thicknesses of these rutile films were investigated in terms of vapor pressure using a variable-angle spectroscopic ellipsometer. As a result, the self-limiting nature in the atomic-layer epitaxy of rutile thin films was demonstrated clearly under various conditions of dosing reactant vapors, where growth rates were almost constant at approximately 0.077 nm/cycle (0.77 nm/min) and refractive indices were also constant at 2.59.