Fabrication of Ordered TiO2 Porous Thin Films by Sol-Dipping PS Template Method

Monolayer polystyrene spheres (∼400 nm) array templates were assembled orderly on clean glass substrates by dip-drawing method from emulsion of PS and porous TiO₂ thin films were prepared by using sol-dipping template method to fill TiO₂ sol into the interstices among the close-packed PS templates and then annealing to remove the PS templates. The effects of TiO₂ precursor sol concentration and dipping time in sol on the porous structure of the thin films were studied. The results showed pore size of the ordered TiO₂ porous thin film depended mainly on PS size and partly on TiO₂ sol concentration. The shrinkage of pore diameter was about 10% for 0.2 M and 20% for 0.4 M TiO₂ sol concentrations. X-ray diffraction (XRD) spectra indicated the porous thin film was anatase structure. The transmittance spectrum showed that optical transmittance of the porous thin film kept above 70% beyond the wavelength of 430 nm. Optical band-gap of the porous TiO₂ thin film (fired at 550^∘;C) was 3.12 eV.