Kationenverteilung und Überstrukturordnung in ternären und quaternären Sulfidspinellen MIIMS4 – Einkristallstrukturuntersuchungen

Cation Distribution and Superstructure Ordering in Ternary and Quaternary Sulfide Spinels M^IIM₂^III S₄ – Single Crystal Structure Determinations The crystal structures of spinel type MIn₂S₄ (M ? Mn, Co, Ni), MCr_2?2xIn_2xS₄ (M ? Mn, Ni), and Cd_0.52Co_0,48Cr₂S₄ were reinvestigated by X-ray methods using single crystals grown by vapour phase transport technique. The indium sulfides possess a partially inverse distribution of the metal ions on the tetrahedral (8a) and octahedral sites (16d) of the structure. The degrees of inversion λ are 0.34 (MnIn₂S₄, a = 1072.0(1) pm, structural parameter u = 0.25726(2)), 0.84 (CoIn₂S₄, a = 1058.1(1) pm, u = 0.26921(5)) und 0.93 (NiIn₂S₄ a = 1050.5(1), u = 0.26040(3)). In the case of the chromium indium sulfide solid solutions, the degrees of inversion (and the structural parameters) increase (and decrease) linearly with increase in indium content x. ψ-scans of reflections not allowed in the space group Fd3 m do not prove simultaneous diffraction. Refinement of the structure of MnIn₂S₄ in space group F4 3m results in a partial superstructure ordering of Mn and In on the tetrahedral sites, 4a Mn_0.83In_0.17, 4c Mn_0.49In_0.51. In the case of Cd_0.52Co_0.48Cr₂S₄, superstructure ordering is like Cd_0.41Co_0.59 and Cd_0.62Co_0.38, respectively.