Effect of Fast Electron Irradiation and Annealing on the Luminescence in GaAs(Zn) crystals. Irradiation-induced 1.26 and 1.39 eV Emission Bands

The effect of 2.2 MeV electron irradiation and subsequent annealings on the photoluminescence in zinc-doped p-type GaAs crystals is studied and analyzed. Rather strong emission bands peaked at hv_m (77 K) near 1.26 eV (induced by electron irradiation) and 1.39 eV (induced by annealing of irradiated crystals) are observed. Evidence is presented that the 1.26 and 1.39 eV emission bands occur due to radiative electronic transitions in As_iZn_Ga and V_AsZn_Ga pairs induced by irradiation and annealing of irradiated crystals, accordingly. The observed variations in the intensities of the 1.26 and 1.39 eV emission bands upon irradiation and subsequent annealings of GaAs(Zn) crystals are explained in terms of irradiation and annealing-induced variations in the amount of 1.26 and 1.39 eV radiative centres resulting from: a) the effective interaction of mobile radiation-induced defects in the arsenic sublattice with zinc atoms leading to the formation of As_iZn_Ga and V_AsZn_Ga pairs; b) the thermal dissociation of As_iZn_Ga and V_AsZn_Ga pairs on individual components.