| Abstract: | Several α-olefins containing the trifluoromethyl group were prepared and characterized. 4,4,4-Trifluoro-1-butene, 3-trifluoromethyl-1-butene, 5,5,5-trifluoro-1-pentene, and 4-trifluoromethyl-1-pentene were homopolymerized with VCl3–Al(i-Bu)3 catalyst. The trifluorobutenes gave low-melting polymers with low fluorine contents. Polymers obtained from the trifluoropentenes were soluble having moderately high intrinsic viscosities. Copolymerizations of these monomers with their nonfluorinated homologs by the same catalyst system indicated low reactivities of the fluoromonomers. Nuclear magnetic resonance spectra of the fluorinated and nonfluorinated monomers and their respective spectroscopic studies with the catalyst (C5H5)2TiCl2–Al(CH3)3 indicated an electron deficiency of the vinyl group of the fluorobutenes. This was related to the inductive effect of the trifluoromethyl group. The inductive effect of this group was absent in the fluoropentenes and the nonfluorinated monomers. The electron-deficient vinyl group of the fluorobutenes apparently did not allow these monomers to coordinate with the active sites of the catalyst. Polymerization studies of the nonfluorinated monomers, 1-butene, 3-methyl-1-butene, 1-pentane, and 4-methyl-1-pentene, with the catalyst VCl3–Al(Bu)3, were performed in the presence of compounds containing the trifluoromethyl group. Results indicated that this group did not retard the rate of polymerization of these monomers. Evidence is presented to show that a catalytic amount of benzotrifluoride enhanced the rate of polymerization of α-olefins, particularly that of sterically hindered monomers such as 3-methyl-1-butene. |