Crystallisation of polypropylene matrix in composites filled with wooden parts of rapeseed straw

Nucleation ability of native and modified rapeseed straw during the polypropylene crystallization from the melt was investigated by the DSC method. Composites were made from isotactic polypropylene and lignocellulosic material using extrusion and injection moulding techniques. They were obtained using polypropylenes differing with respect to melt flow rates and different varieties of rapeseed straw. Chemical modification was carried out in two stages: through mercerisation and treatment with acetic acid anhydride. In the course of investigations, it was found that both native and modified rapeseed straw acted as an active nucleant of polypropylene crystallisation characterised by low values of MFR indices. It was found that for polypropylenes with high MFR values, the values of crystallization temperatures and crystallization half-time in composites were identical when compared with non-filled polymers. The investigations demonstrated that there were insignificant differences among composites containing straw from different varieties of rapeseed. The analysis of crystallization temperatures confirmed that rapeseed straw modification failed to change this parameter of the crystallization process. A similar tendency was observed in the case of changes of the half-time crystallization process. Moreover, the analysis of the crystallization temperature and crystallization half-time showed that the presence in composites of lignified rapeseed straw particles played an important role in the crystallization conditions.