Preparation and characterization of glasses in the Ag2S + B2S3 + GeS2 system

The glass forming range of the Ag₂S + B₂S₃ + GeS₂ ternary system was investigated for the first time and a wide range of ternary glasses were obtained. The Archimedes’ method was used to determine the densities of the Ag-B-Ge glasses. The thermal properties of these thioborogermanate glasses were studied by DSC and TMA. The Raman, IR and NMR spectroscopy were used to explore the short-range order structure of the binary (Ag-B) and (Ag-Ge) and ternary (Ag-B-Ge) glasses. The results show the presence of bridging sulfur tetrahedral units, GeS_4/2 and AgBS_4/2, and trigonal units, BS_3/2, in the ternary glasses. Non-bridging sulfur units, AgSGeS_3/2 and Ag₃B₃S₃S_3/2 six membered rings, are also observed in these glasses at higher Ag₂S modification levels because the further addition of Ag₂S results in the degradation of the bridging structures to form non-bridging structures. The NMR studies show that Ag₂S goes into the GeS₂ subnetwork to form Ag₃S₃GeS_1/2 groups before going to the B₂S₃ subnetwork. In doing so, it is suggested that B₁₀S₂₀ supertetrahedra exist in Ag₂S + B₂S₃ and Ag₂S + B₂S₃ + GeS₂ glasses. Significantly B-S-Ge bonds form in the B₂S₃ + GeS₂ glasses, whereas they appear to be absent in the ternary glasses. From these observations, a structural model for these glasses has been developed and proposed.