The thermodynamic parameters of oxygen nonstoichiometry defects in lanthanum cobaltite doped with acceptor impurities (Sr and Ni)

The oxygen nonstoichiometry δ of lanthanum cobaltite doped with acceptor impurities (Sr and Ni), La_{1 ? x} Sr_xCo_0.9Ni_0.1O_{3 ? δ} (x = 0.1, 0.3), was studied by high-temperature thermogravimetry over the temperature and pressure ranges 723 K ≤ T ≤ 1373 K and 10^?3 atm ≤ $p_{O_2 } $ ≤ 1 atm. The partial replacement of cobalt with nickel and lanthanum with strontium increased the oxygen nonstoichiometry δ. The partial molar enthalpies $Delta bar H^circ _O $ and entropies $Delta bar S^circ _O $ of solution of oxygen in the solid phase were calculated. Models of point defect formation were suggested and analyzed. The equilibrium constants of formation and concentrations of predominant point defects, ionized oxygen vacancies V _o ^.. , holes Me _Co ^. (Co _Co ^. and Ni _Co ^. ), and electrons Me _Co ^′ (Co _Co ^′ and Ni _Co ^′ ) localized on 3d transition metals, were determined by nonlinear regression from the experimental and theoretical logp $p_{O_2 } $ ?δ dependences.