New ferromagnetic La3Co2TaO9 double perovskite: Structural and magnetic properties

The new double perovskite La₃Co₂TaO₉ has been prepared by a solid-state procedure. The crystal and magnetic structures have been studied from X-ray powder diffraction (XRPD) and neutron powder diffraction (NPD) data. Rietveld refinements were performed in the monoclinic space group P2₁/n. The structure consists of an ordered array of alternating B′O₆ and B″O₆ octahedra sharing corners, tilted along the three pseudocubic axes according to the Glazer notation a⁻b⁻c⁺. Rietveld refinements show that at RT the cell parameters are a=5.6005(7) Å, b=5.6931(7) Å, c=7.9429(9) Å and β=89.9539(7)°, and the refined crystallographic formula of this “double perovskite” can be written as La₂(Co)_2d(Co_1/3Ta_2/3)_2cO₆. Magnetization measurements and low-temperature NPD data show that the perovskite is a ferromagnet with T_C=72 K. At high T it follows the Curie–Weiss law with an effective magnetic moment of 3.82μ_B per Co ion which is very close to spin only Co²⁺ (HS).