Enhanced energy storage in polyvinylidenefluoride (PVDF) + BaZrO3 electroactive nanocomposites

PVDF + BaZrO₃ electroactive nanocomposite thin film has been prepared by solution casting method. The structural analysis was carried out by using x-ray diffraction pattern and atomic force microscopy (AFM). Generally, the performance of dielectric capacitors toward higher energy density and higher operating temperatures has been drawing increased interest. In this regard, the present study was focussed on the fabrication and characterization of PVDF + BaZrO₃ electroactive nanocomposites in view of enhancing the energy density at elevated temperature. Cole-Cole plot is an agreement with multiple relaxation process in electroactive nanocomposites. Dielectric energy storage performance is assessed for PVDF nanocomposites with different wt% of BaZrO₃ at different frequencies and temperature. It has been observed that with increase of temperature, the permittivity increased while the energy density slightly decreased but significantly higher than pure polymer PVDF. A high energy density of 6.88 J/cm³ was obtained for BaZrO₃ electroactive nanocomposites at 50 °C and 5.06 J/cm³ at 70 °C. Overall, the testing results indicate that using nanocomposites of PVDF and BaZrO₃ as a dielectric component is promising for implementation to preserve high energy density values up to temperatures of 70 °C.The enhancement of dielectric permittivity and the energy density is attributed due to increase of interracial charge density. The effect of BaZrO₃ nanoparticles in energy density of PVDF is first time reported.