| 摘 要： | 本文利用SEM表征了低压铝电解电容器用高比容腐蚀箔的结构,采用立方孔模型建立了低压腐蚀化成箔的结构-性能关系,并通过压汞仪测试对所建模型进行验证。SEM结果表明,低压腐蚀箔呈现海绵状结构,蚀坑保持立方型孔洞。在实用情况下,对于22. 4 V化成电压,最适孔径为0. 20~0. 24μm,最大比容为(185. 3~227. 6)×10^-6F·cm^-2。压汞仪测试结果表明,建立的立方孔洞模型可以反映低压腐蚀箔结构特征。
|
| 关 键 词： | 铝电解电容器 低压阳极箔 立方孔洞模型 比容 构效关系 压汞仪 |
Structure-property relationship of anode foil for low-voltage aluminum electrolytic capacitor |
| |
| CHEN Jinxiong,FANG Mingqing,HE Fengrong,TENG Shiguo,XIAO Yuanlong.Structure-property relationship of anode foil for low-voltage aluminum electrolytic capacitor[J].Electronic Components & Materials,2020(1):37-41. |
| |
| Authors: | CHEN Jinxiong FANG Mingqing HE Fengrong TENG Shiguo XIAO Yuanlong |
| |
| Institution: | (Ruyuan Yao Autonomous Dongyangguang Forming Foil Co.,Ltd,Shaoguan 512721,Guangdong Province,China;Dongguan Dongyangguang Research and Development Co.,Ltd,Dongguan 523871,Guangdong Province,China;Ruyuan Dongyangguang Machinery Co.,Ltd,Shaoguan 512721,Guangdong Province,China) |
| |
| Abstract: | The structure of low-voltage etching foil with high specific capacitance for aluminum electrolytic capacitor was characterized by SEM,and then a cubic pit model was adopted to study the structure-property relationship of the foil. The so-built model was verified by the mercury porosimetry. The results show that the etching foil has a sponge like cubic pit structure. The optimal diameter and maximum capacitance at forming voltage of 22. 4 V for practical application is 0. 20-0. 24μm and( 185. 3-227. 6) × 10^-6 F·cm^-2,respectively. Furthermore,the mercury porosimetry result shows that the cubic pit model can reflect the structural characteristic of low-voltage etching foil. |
| |
| Keywords: | aluminum electrolytic capacitor low-voltage anode foil cubic pit model specific capacitance structure-property relationship mercury intrusion meter |