Stress overshoot of polymer solutions at high rates of shear; Polystyrene with bimodal molecular weight distribution

Overshoot of shear stress, σ, and the first normal stress difference, N₁, in shear flow was investigated for dilute solutions of polystyrene with very high molecular weight in concentrated solution of low M PS. In the case that the matrix was a nonentangled system, behavior of overshoot was similar to that of dilute solution of high M PS in pure solvent. The magnitudes of shear, γ_σm and γ_Nm, corresponding to the peaks of σ and N₁ lay on the universal functions of γ˙τ_R, respectively, proposed for dilute solutions in pure solvent. Here τ_R is the Rouse relaxation time for high M PS in the blend evaluated from dynamic modulus at high frequencies. In the case that the matrix was an entangled system, an additional σ peak was observed at high rates of shear at times corresponding to γ_σm = 2–3. This peak can be assigned to the motion of low M chains in entanglement network. When the matrix was entangled, stress overshoot was observed even at relatively low rates of shear, say γ˙τ_R < 10^?2. This is probably due to the motion of high M chains in entanglement of all the chains. In this case the γ_σm and γ_Nm values were higher than those expected for entangled chains of monodisperse polymer in pure solvent. © 2000 John Wiley & Sons, Inc. J Polym Sci B: Polym Phys 38: 2043–2050, 2000