Deposition and characterization of binary Al2O3/SiO2 coating layers on the surfaces of rutile TiO2 and the pigmentary properties

Binary Al₂O₃/SiO₂-coated rutile TiO₂ composites were prepared by a liquid-phase deposition method starting from Na₂SiO₃·9H₂O and NaAlO₂. The chemical structure and morphology of binary Al₂O₃/SiO₂ coating layers were investigated by Fourier transform infrared spectroscopy, X-ray photoelectron spectroscopy, TG-DSC, Zeta potential, powder X-ray diffraction, and transmission electron microscopy techniques. Binary Al₂O₃/SiO₂ coating layers both in amorphous phase were formed at TiO₂ surfaces. The silica coating layers were anchored at TiO₂ surfaces via Si-O-Ti bonds and the alumina coating layers were probably anchored at the SiO₂-coated TiO₂ surfaces via Al-O-Si bonds. The formation of continuous and dense binary Al₂O₃/SiO₂ coating layers depended on the pH value of reaction solution and the alumina loading. The binary Al₂O₃/SiO₂-coated TiO₂ composites had a high dispersibility in water. The whiteness and brightness of the binary Al₂O₃/SiO₂-coated TiO₂ composites were higher than those of the naked rutile TiO₂ and the SiO₂-coated TiO₂ samples. The relative light scattering index was found to depend on the composition of coating layers.