Microporous Silica Xerogel Membrane with High Selectivity and High Permeance for Carbon Dioxide Separation

The asymmetric microporous silica xerogel membrane was prepared by sol-gel method. A multi-layer (asymmetric) structure was obtained by silica xerogel layer on top of mesoporous silica layer (mean pore diameter of 4 nm), supported by porous alumina tube (mean pore diameter of 0.1 m). The ratio of the permeances, CO₂/N₂ for this membrane attained more than 60 at 298 K. This value is considerably higher than the theoretical Knudsen value (CO₂/N₂ = 0.8). The gas permeances of this membrane were about 5–10 times higher than the previous membrane. Application of the membrane to an enrichment of CO₂ from air was also investigated. CO₂ in the air (about 300 ppm) was concentrated to more than 1000 ppm by using the membrane at 298 K.