Crystal-field studies of trivalent Thulium in Yttrium Aluminum Garnet |
| |
| Authors: | J A Koningstein |
| |
| Institution: | (1) E. W. R. Steacie Building of Chemistry, Carleton University, Ottawa, Ontario, Canada |
| |
| Abstract: | CF parameters have been calculated from the splitting of some of the manifolds of Tm3+ in Yttrium Aluminum Garnet (YAlG). Values of these parameters are: A
2
0
=270 cm–1, A
2
2
=± 95 cm–1, A
4
0
=–170 cm–1, A
4
2
=± 410 cm–1, A
4
4
=–1020 cm–1, A
6
0
=30 cm–1, A
6
2
=± 115 cm–1, and A
6
4
=–475 cm–1. There are indications that these parameters do not describe the splitting patterns of excited states with higher energy.
Zusammenfassung Aus der Aufspaltung entarteter Zustände von Tm3+ in YAlG sind Kristallfeldparameter berechnet worden. Die Werte dieser Parameter sind: A
2
0
=270 cm–1, A
2
2
=± 95 cm–1, A
4
0
=–170 cm–1, A
4
2
=± 410 cm–1, A
4
4
=–1020 cm–1, A
6
0
=30 cm–1, A
6
2
=± 115 cm–1, und A
6
4
=–475 cm–1. Es gibt Anzeichen dafür, daß diese Parameter nicht das Aufspaltungsmuster angeregter Zustände höherer Energie beschreiben.
Résumé On a calculé les paramètres du champ cristallin à partir de la séparation obtenue par levée de dégénerescence pour les niveaux de Tm3+ dans le grenat d'yttrium aluminium (YAlG). Les valeurs de ces paramètres sont: A
2
0
=270 cm–1, A
2
2
=±95 cm–1, A
4
0
=–170 cm–1, A
4
2
= ± 410 cm–1, A
4
4
=–1020 cm–1, A
6
0
=30 cm–1, A
6
2
=± 115 cm–1 et A
6
4
=–475 cm–1. Il existe des indications selon lesquelles ces paramètres ne décrivent pas l'aspect des séparations des états excités d'énergies plus élevées. |
| |
| Keywords: | |
| 本文献已被 SpringerLink 等数据库收录！ |
|