Tuning the π‐π stacking distance and J‐aggregation of DPP‐based conjugated polymer via introducing insulating polymer |
| |
| Authors: | Liang Chen Haiyang Wang Jiangang Liu Rubo Xing Xinhong Yu Yanchun Han |
| |
| Institution: | 1. State Key Laboratory of Polymer Physics and Chemistry, Changchun Institute of Applied Chemistry, Chinese Academy of Sciences, Changchun, People's Republic of China;2. University of the Chinese Academy of Sciences, Beijing, People's Republic of China |
| |
| Abstract: | The close π–π stacking and the high J‐aggregation during the formation of fibrillar morphology in films of the poly2,5‐bis(2‐octyldodecyl)?2,3,5,6‐tetrahydro‐3,6‐dioxopyrrolo3,4‐c]pyrrole‐1,4‐diyl]‐alt–2,2′‐(2,5‐thiophene)bis‐thieno3,2‐b]thiophen]‐5,5′‐diyl]] (PDPPTT‐T) are demonstrated via blending with polystyrene (PS). The hydrodynamic radius (Rh) of PDPPTT‐T is decreased from 16.7 nm in the neat solution to 12.7 nm in the blend solution at the ratio of 1/20(PDPPTT‐T/PS). This phenomenon suggests that blending PS is beneficial for the disentanglement of PDPPTT‐T. The disentanglement of PDPPTT‐T facilitates the formation of fibrillar morphology. The growth of the fibrils occurs along the molecular backbones and the width of the fibrils is parallel to the π–π stacking direction. The disentanglement of PDPPTT‐T helps the molecules adjust conformation to improve J‐aggregation and decrease the π–π stacking distance. The maximum absorption is red‐shifted from 825 nm to 849 nm and the relative intensity of J‐aggregation (the 0‐0/0‐1 ratio) is increased from 1.19 to 1.60. The π–π stacking distance decreases from 3.57 to 3.52 Å. The charge‐carrier mobility will be improved in the fibrillar morphology with close π–π stacking and high J‐aggregation. © 2016 Wiley Periodicals, Inc. J. Polym. Sci., Part B: Polym. Phys. 2016 , 54, 838–847 |
| |
| Keywords: | blends conjugated polymers disentanglement morphology J‐aggregation π – π stacking distance |
|
|