| 添加Al2O3对Ni0.5Zn0.5Fe2O4纳米纤维结构和磁性能的影响 | |
| 引用本文： | 向 军,周广振,褚艳秋,郭银涛,沈湘黔.添加Al2O3对Ni0.5Zn0.5Fe2O4纳米纤维结构和磁性能的影响[J].无机化学学报,2011,27(10):1959-1963. |
| 作者姓名： | 向 军 周广振 褚艳秋 郭银涛 沈湘黔 |
| 作者单位： | 1. 江苏科技大学数理学院,镇江212003;江苏大学材料科学与工程学院,镇江212013 2. 江苏科技大学数理学院,镇江,212003 3. 江苏大学材料科学与工程学院,镇江,212013 |
| 基金项目： | 国家自然科学基金(No.50674048); 高等学校博士学科点专项科研基金(No.20103227110006); 江苏省高校自然科学基金(No.11KJB430006); 江苏省青蓝工程资助项目 |
| 摘 要： | 采用静电纺丝技术制备了添加0～20wt%Al2O3的Ni0.5Zn0.5Fe2O4纳米纤维。通过XRD、FESEM、TEM和VSM对样品的物相结构、形貌和磁性能进行了表征。结果表明,所合成的复合纳米纤维的直径都分布在40～150 nm之间,添加到纤维中的Al2O3主要以非晶态形式分布于铁氧体晶粒边界;随着Al2O3添加量的增加,可观察到γ-Fe2O3相逐渐析出,Ni-Zn铁氧体的晶格常数单调减小,说明有一些Al2O3进入到尖晶石晶格中取代了B位的Fe3+离子,Ni-Zn铁氧体的平均晶粒尺寸先增大后减小,在Al2O3添加量为8wt%时达到最大值39.2 nm;比饱和磁化强度和矫顽力随Al2O3添加量的增加呈现出相同的变化规律,先减小后增大,当Al2O3添加量超过5wt%时又开始变小。 |
| 关 键 词： | Ni-Zn铁氧体 Al2O3 纳米纤维 静电纺丝 |
Effect of Al2O3 Addition on Structural and Magnetic Properties of Ni0.5Zn0.5Fe2O4 Nanofibers |
|
| XIANG Jun,ZHOU Guang-Zhen,CHU Yan-Qiu,GUO Yin-Tao and SHEN Xiang-Qian.Effect of Al2O3 Addition on Structural and Magnetic Properties of Ni0.5Zn0.5Fe2O4 Nanofibers[J].Chinese Journal of Inorganic Chemistry,2011,27(10):1959-1963. | |
| Authors: | XIANG Jun ZHOU Guang-Zhen CHU Yan-Qiu GUO Yin-Tao and SHEN Xiang-Qian |
| Institution: | School of Mathematics and Physics, Jiangsu University of Science and Technology, Zhenjiang, Jiangsu 212003, China; School of Material Science and Engineering, Jiangsu University, Zhenjiang, Jiangsu 212003, China,School of Mathematics and Physics, Jiangsu University of Science and Technology, Zhenjiang, Jiangsu 212003, China,School of Mathematics and Physics, Jiangsu University of Science and Technology, Zhenjiang, Jiangsu 212003, China,School of Mathematics and Physics, Jiangsu University of Science and Technology, Zhenjiang, Jiangsu 212003, China and School of Material Science and Engineering, Jiangsu University, Zhenjiang, Jiangsu 212003, China |
| Abstract: | Ni0.5Zn0.5Fe2O4 nanofibers with the addition of different weight percents of Al2O3 in the range 0 to 20wt% were fabricated by electrospinning technique.The phase structure,morphology and magnetic properties of the samples were characterized by XRD,field emission scan electron microscopy(FESEM),TEM and vibrating sample magnetometer(VSM).The results show that the diameters of the synthesized composite nanofibers range from 40 to 150 nm.The Al2O3 added into the nanofibers mainly tend to distribute on the grain... |
| Keywords: | Ni-Zn ferrite Al2O3 nanofiber electrospinning |