Synthesis and characterization of poly(vinyl phosphonic acid) (PVPA)-Fe3O4 nanocomposite

Poly(vinyl phosphonic acid) (PVPA)-Fe₃O₄ nanocomposite is synthesized by the precipitation of Fe₃O₄ in the presence of PVPA. Structural, surface, morphological, thermal properties and conductivity characterization/evaluation of the nanocomposite were performed by XRD, FT-IR, TEM, TGA and conductivity measurements respectively. The capping of PVPA around the Fe₃O₄ nanoparticles was confirmed by FT-IR spectroscopy, the interaction being via bridging oxygens of the phosphate and the nanoparticle surface. The crystallite and particle size were obtained as 6 ± 2 and 8.7 ± 0.1 nm from XRD line profile fitting and TEM image analysis respectively, which reveal nearly single crystalline nature of the Fe₃O₄ nanoparticles. Magnetic characterization of the bulk magnetite and (PVPA)-Fe₃O₄ nanocomposite reveals that both are in the superparamagnetic state at room temperature. The average magnetic domain size of the nanoparticles has been calculated using the Langevin function, which was fitted to the measured M-H hysteresis curves as 7.6 nm for the nanocomposite. In the nanocomposite, the reduction is due to the adsorption of PVPA onto the magnetite surface, which cancels some of the free spins at the surface causing a magnetically dead layer. Analysis of the conductivity and permittivity measurements revealed the coupling of ionic and polymer segmental motions and strong temperature dependency in the nanocomposite.