Temperature- and pressure-responsive properties of l- and dl-forms of poly(N-(1-hydroxymethyl)propylmethacrylamide) in aqueous solutions

The structural transition of the l- and dl forms of poly(N-(1- hydroxymethyl)propylmethacrylamide (PHMPMA) in aqueous solution was studied by measuring the pressure dependence of the apparent scattering intensity, differential scanning calorimetry (DSC), and circular dichroism (CD). The thermodynamic implications of the results are discussed in relation to the chiral structure of the side chain, and differences in the thermal and barometric transitions. T-P diagrams of the transition showed characteristic ellipsoid features. Antagonism of the temperature and pressure effects was observed only for P(dl-HMPMA). For P(l-HMPMA), the transition temperature (T_tr) decreased with increasing pressure, and the highest T_tr was observed at atmospheric pressure (0.1 MPa). For both polymers, the highest P_trs were observed at the lowest temperatures. The l polymer showed a specific negative peak in its CD spectrum at around 220 nm in the lower temperature region and the temperature dependence was reproduced by a single-step transition, with the midpoint corresponding to the T_tr obtained from the scattering measurements. Coupled with the results from the DSC, the different behavior between the P(l-HMPMA) and P(dl-HMPMA) could be explained in terms of the chain states before and after the transition. The cooperative factors derived from the DSC measurement revealed that about 4 to 5 polymers of the present size were necessary to perform a thermal transition for P(l-HMPMA), and that P(dl-HMPMA) underwent its transition as an almost single molecular event.This revised version was published online in June 2005 with correction to the article category.