Morphology and transmittance of porous alumina on glass substrate |
| |
Authors: | Guo Peitao Xia Zhilin Xue YiyuHuang Caihua Zhao Lixin |
| |
Institution: | a Wuhan University of Technology. Wuhan, China b Key Laboratory of Low Dimensional Materials & Application Technology, Xiangtan University, Ministry of Education, Xiangtan, China c China Three Gorges University, Yichang, China |
| |
Abstract: | The porous optical film has higher threshold of laser-induced damage than densified films, for the study of mechanism of laser-induced damage of porous optical film with ordered pore structure. Porous anodic alumina (PAA) film with high transmittance on glass substrate has been prepared. Aluminum film was deposited on glass substrate by means of resistance and electron beam heat (EBH) evaporation. Porous alumina was prepared in oxalic acid solution under different anodizing conditions. At normal incidence, the optical transmittance spectrum over 300-1000 nm spectra region was obtained by spectrophotometer. SEM was introduced to analysis the morphology of the porous alumina film. The pore aperture increased with the increase of anodizing voltage, which resulted in a rapid decrease of the pore concentration and the optical thickness of porous alumina film. Damage morphology of porous alumina film is found to be typically defects initiated, and the defect is the pore presented on the film. |
| |
Keywords: | Porous alumina Glass substrate Optical property Laser-induced damage Morphology |
本文献已被 ScienceDirect 等数据库收录! |
|