Luminescence characterization and electron beam induced chemical changes on the surface of ZnAl2O4:Mn nanocrystalline phosphor

Luminescence characteristics and surface chemical changes of nanocrystalline Mn²⁺ doped ZnAl₂O₄ powder phosphors are presented. Stable green cathodoluminescence (CL) or photoluminescence (PL) with a maximum at ∼512 nm was observed when the powders were irradiated with a beam of high energy electrons or a monochromatic xenon lamp at room temperature. This green emission can be attributed to the ⁴T₁ → ⁶A₁ transitions of the Mn²⁺ ion. Deconvoluted CL spectra resulted in two additional emission peaks at 539 and 573 nm that may be attributed to vibronic sideband and Mn⁴⁺ emission, respectively. The luminescence decay of the Mn²⁺ 512 nm emission under 457 nm excitation is single exponential with a lifetime of 5.20 ± 0.11 ms. Chemical changes on the surface of the ZnAl₂O₄:Mn²⁺ phosphor during prolonged electron beam exposure were monitored using Auger electron spectroscopy. The X-ray photoelectron spectroscopy (XPS) was used to determine the chemical composition of the possible compounds formed on the surface as a result of the prolonged electron beam exposure. The XPS data suggest that the thermodynamically stable Al₂O₃ layer was formed on the surface and is possibly contributing to the CL stability of ZnAl₂O₄:Mn phosphor.