| Fabrication and Performance of a Low Operating Pressure Nanofiltration Poly（vinyl chloride） Hollow Fiber Membrane |
| |
| 引用本文： | 朱宝库.Fabrication and Performance of a Low Operating Pressure Nanofiltration Poly（vinyl chloride） Hollow Fiber Membrane[J].高分子科学,2014,32(3):377-384. |
| |
| 作者姓名： | 朱宝库 |
| |
| 作者单位： | MOE Key Laboratory of Macromolecular Synthesis and Functionalization,MOE Engineering Research Center of Membrane and Water Treatment Technology, Department of Polymer Science and Engineering, Zhejiang University, Hangzhou 310027, China |
| |
| 基金项目： | This work was financially supported by the National Natural Science Foundation of China （No. 20974094）, National 973 Program （No. 2009CB623402）, and Postdoctoral Science Foundation funded project of Zhejiang Province, China （Bsh1202045）. |
| |
| 摘 要： | A low operating pressure nanofiltration membrane is prepared by interfacial polymerization between m-phenylenediamine(MPDA) and trimesoyl chloride(TMC) using PVC hollow fiber membrane as supporting.A series of PVC nanofiltration membranes with different molecular weight cutoff(MWCO) can be obtained by controlling preparation conditions.Chemical and morphological characterization of the membrane surface was carried out by FTIR-ATR and SEM.MWCO was characterized by filtration experiments.The preparation conditions were investigated in detail.At the optimized conditions(40 min air-dried time,aqueous phase containing 0.5% MPDA,0.05% SDS and 0.6% acid absorbent,oil phase containing 0.3% TMC,and 1 min reaction time),under 0.3 MPa,water flux of the gained nanofiltration membrane reaches 17.8 L/m2·h,and the rejection rates of methyl orange and MgSO4 are more than 90% and 60%,respectively.
|
| 关 键 词： | 中空纤维膜 纳滤膜 工作压力 氯乙烯 FTIR-ATR 截留分子量 性能 制造 |
Fabrication and performance of a low operating pressure nanofiltration poly(vinyl chloride) hollow fiber membrane |
| |
| Jian-hua Wang,Yue-li Wu,Yong-hua Zhang,Bao-ku Zhu,You-yi Xu.Fabrication and performance of a low operating pressure nanofiltration poly(vinyl chloride) hollow fiber membrane[J].Chinese Journal of Polymer Science,2014,32(3):377-384. |
| |
| Authors: | Jian-hua Wang Yue-li Wu Yong-hua Zhang Bao-ku Zhu You-yi Xu |
| |
| Institution: | 1. MOE Key Laboratory of Macromolecular Synthesis and Functionalization, MOE Engineering Research Center of Membrane and Water Treatment Technology, Department of Polymer Science and Engineering, Zhejiang University, Hangzhou, 310027, China
|
| |
| Abstract: | A low operating pressure nanofiltration membrane is prepared by interfacial polymerization between m-phenylenediamine (MPDA) and trimesoyl chloride (TMC) using PVC hollow fiber membrane as supporting. A series of PVC nanofiltration membranes with different molecular weight cutoff (MWCO) can be obtained by controlling preparation conditions. Chemical and morphological characterization of the membrane surface was carried out by FTIR-ATR and SEM. MWCO was characterized by filtration experiments. The preparation conditions were investigated in detail. At the optimized conditions (40 min air-dried time, aqueous phase containing 0.5% MPDA, 0.05% SDS and 0.6% acid absorbent, oil phase containing 0.3% TMC, and 1 min reaction time), under 0.3 MPa, water flux of the gained nanofiltration membrane reaches 17.8 L/m2·h, and the rejection rates of methyl orange and MgSO4 are more than 90% and 60%, respectively. |
| |
| Keywords: | PVC Interracial polymerization Nanofiltration membrane Hollow fiber membrane |