Dehydration and crystallization process in sol-gel zirconia

Sol-gel zirconia was characterized using high-resolution thermogravimetry (Hi-Res TG) and differential scanning calorimetry (DSC) and compared with X-ray diffraction, Raman scattering, and UV-Vis spectroscopy. ZrO_2-x(OH)_2x·yH₂O annealed below 400°C show typical behavior of amorphous material. As the annealing temperature is increased, the tetragonal and monoclinic phases crystallize. Typical Hi-Res TG curve shows that the samples are continuously dehydrated in a long temperature range, between room temperature and 600°C. The total mass loss relative to the initial mass is of about 29%. The DSC analysis coupled with TG and structural information, indicate that the exothermic processes about 355 and 447°C can be related to the nucleation process of the formation of tetragonal zirconia, with bulk crystallization at 447°C. This revised version was published online in July 2006 with corrections to the Cover Date.