Characterization of dental composites by thermal analysis, infrared spectroscopy and scanning electron microscopy

Commercial light-cured dental composites were used in this study. Two laboratorial composites, Resilab (Wilcos/Brazil), Epricord (Kuraray/Japan) were compared under cured and uncured conditions. Thermal analysis, infrared spectroscopy and scanning electron microscopy were used to evaluate the dental composites. The mass change and heat flow signals (TG–DSC) were recorded simultaneously by using STA 409 PC Luxx (NETZSCH), in the 25–800 °C temperature range at a heating rate of 10 °C/min under nitrogen atmosphere (70 mL/min). Employing thermo-microbalance TG 209 C F1 Iris (NETZSCH) coupled to the BRUKER Optics FTIR TENSOR, the samples were analyzed by combined thermogravimetric and spectroscopic methods (TG–FTIR). The initial sample mass was about ~12 mg, the data collection have been done in the 35–800 °C temperature range at a heating rate of 20 K/min in nitrogen atmosphere (flow rate: 40 mL/min). Finally, superficial topographic was analyzed by scanning electron microscopy (SEM). Dental composite evaluation suggests a high thermal stability and inorganic content in RES D sample. Degrees of conversion (DC) values were almost the same and there was no direct relationship between DC and amount of particles and size. Similar compositions were found in all samples.