Hierarchical nanoporous structures are fabricated by adsorption of micelles of diblock copolymer‐templated Au‐nanoparticles onto a hydrophilic solid substrate. Gold nanoparticles are prepared using micelles (19 nm) of polystyrene‐block‐poly(4‐vinylpyridine) (PS‐b‐P4VP) as nanoreactors. Deposition of thin films of the micellar solution, modified with a non‐selective solvent (THF), on hydrophilic surfaces leads to the formation of hierarchical nanoporous morphologies. The thin films exhibit two different pore diameters and a total pore density of 15 × 108 holes per cm2. The structure was analyzed in terms of topography and chemical composition using AFM, TEM and XPS measurements. The PS‐b‐P4VP template was subsequently removed by oxygen plasma etching, to leave behind metallic nanopores that mimic the original thin film morphology.