Solid State NMR and TG/MS Study on the Transformation of Methyl Groups During Pyrolysis of Preceramic Precursors to SiOC Glasses

The sol-gel method was used to prepare two different starting gels containing SiCH₃-groups for the preparation of SiOC ceramics. To understand the role of Si—H bonds in the incorporation of carbon into the SiOC network, gels prepared from a 1:2 mixture of triethoxysilane and methyldiethoxysilane (T^HD^H2) and solely methyltriethoxysilane (T^Me) were investigated. Thermogravimetric analysis coupled with mass spectroscopy (TG-MS) in inert atmosphere was performed to attain an insight into the decomposition reactions involved during gel-glass transformation. Samples calcined at different temperatures up to 1000°C were characterized by ²⁹Si and ¹³C magic angle spinning nuclear magnetic resonance (MAS-NMR) spectroscopy. The presence of SiH groups in the starting gel allows an efficient conversion of Si—CH₃ groups into CSi₄ sites at lower temperatures. As a result, despite a much lower amount of carbon in the starting T^HD^H2 gel (C/Si = 0.33) compared to the T^Me gel (C/Si = 1), the amount of carbon inserted into the SiOC network of both glasses is equivalent, but the T^Me sample contains the 10 fold amount of free carbon.