Conversion of yttrium-aluminum garnet to soluble forms as a result of mechanochemical treatment

Summary The changes in the solubility and in the phase composition of yttrium-aluminum garnet (YAG) as a result of its mechanochemical treatment for 2 h in a planetary ball mill together with H₃BO₃ and Na₂CO₃ (mole ratio H₂BO₃/Na₂CO₃=4) in ratios (H₃BO₃+Na₂CO₃)/YAG=2,4, and 9 are studied. At a ratio of 9, the yield of yttrium in the water solution obtained upon treatment of the activated mixture at 90 °C (50 cm³ water/g sample) reaches 85%. Its content in the same solution is above 93% relatively to the sum Y+Al.

---

Umwandlung von Yttrium-Aluminium-Granat in lösliche Formen durch mechanochemische Behandlung

Zusammenfassung Die Änderungen bezüglich Löslichkeit und Phasenzusammensetzung von Yttrium-Aluminium-Granat (YAG) als Ergebnis einer zweistündigen mechanochemischen Behandlung in einer Kugelmühle zusammen mit H₃BO₃ und Na₂CO₃ (Molverhältnis H₃BO₃/Na₂CO₃=4) bei (H₃BO₃+Na₂CO₃)/YAG-Verhältnissen von 2, 4 und 9 wurden untersucht. Bei einem Verhältnis von 9 erreicht die Ausbeute an Yttrium in der wäßrigen Lösung nach Behandlung der aktivierten Mischung bei 90 °C (50 cm³ H₂O pro Gramm) 85%. Relativ zur Summe Y+Al beträgt der Yttriumgehalt 93%.