Infrared Spectroscopic Studies on the Surface Chemistry of High‐Surface‐Area Gallia Polymorphs

Polymorphs α, β, and γ of Ga₂O₃ having hexagonal (corundum‐type), monoclinic and cubic (spinel‐type) structure, respectively, were prepared in a high‐surface‐area form, and characterized by powder X‐ray diffraction. Nitrogen adsorption at 77 K showed these gallia samples to have specific surface areas of 77 (α‐Ga₂O₃), 40 (β‐Ga₂O₃) and 120 m² g^?1 (γ‐Ga₂O₃). Fourier transform infrared spectroscopy of adsorbed carbon monoxide (at 77 K) and pyridine (at room temperature) showed that the three gallia polymorphs have a very similar surface Lewis acidity, regardless of their different crystal structures. This Lewis acidity was assigned, mainly, to coordinatively unsaturated tetrahedral Ga³⁺ ions situated on the surface of the small crystallites which constitute the different metal oxide varieties. Ga³⁺···CO adducts formed after CO adsorption gave (in all cases) a characteristic C–O stretching band at 2195–2200 cm^?1, while Lewis‐type adducts formed with adsorbed pyridine were characterized by IR absorption bands at 1610–1612 and 1446–1450 cm^?1. The three (partially hydroxylated) gallia polymorphs showed also a very weak Brønsted acidity, which they manifested by forming hydrogen‐bonded adducts with both CO and pyridine; however no protonation of adsorbed pyridine occurred.