Corrosion inhibition of steel in 0.5 M H2SO4 by [(2-pyridin-4-ylethyl)thio]acetic acid

The influence of [(2-pyridin-4-ylethyl)thio]acetic acid (P1) and pyridine (P2) on the corrosion inhibition of steel in sulphuric acid solution is studied using weight loss, potentiodynamic polarisation and linear polarisation resistance (R_p) and electrochemical impedance spectroscopy (EIS) measurements. Results obtained show that P1 is the best inhibitor and its inhibition efficiency (E%) increases with the increase of concentration. The highest E% of 82% is observed at 5 × 10⁻³ M. Potentiodynamic polarisation studies clearly reveal that P1 acts as a mixed inhibitor. The inhibitor studied reduces the corrosion rates. E% values obtained from various methods used are in good agreement. Adsorption of P1 on steel surface obeys to Langmuir adsorption isotherm. Effect of temperature indicates that E% decreases with temperature between 298 and 353 K.