Multiple melting behavior in isothermally crystallized poly(trimethylene terephthalate)

Melting behavior of poly(trimethylene terephthalate) (PTT) after isothermal crystallization from the melt state was studied using differential scanning calorimetry (DSC) and wide-angle X-ray diffraction (WAXD) techniques. The subsequent melting thermograms for PTT isothermally crystallized within the temperature range of 182-215 °C exhibited triple (for crystallization temperatures lower than ≈192 °C), double (for crystallization temperatures greater than ≈192 °C but lower than ≈210 °C), or single (for crystallization temperatures greater than ≈210 °C) endothermic melting phenomenon. These peaks were denoted peaks I, II, and III for low-, middle-, and high-temperature melting endotherms, respectively. For the triple melting phenomenon, it was postulated that the occurrence of peak I was a result of the melting of the primary crystallites, peak II was a result of the melting of recrystallized crystallites, and peak III was a result of the melting of the recrystallized crystallites of different stabilities. In addition, determination of the equilibrium melting temperature T_m⁰ for this PTT resin according to the linear and non-linear Hoffmann-Weeks extrapolation provided values of 243.6 and 277.6 °C, respectively.