Synthesis, crystal structure and magnetic properties of the open framework compound Co3Te2O2(PO4)2(OH)4

The new compound Co₃Te₂O₂(PO₄)₂(OH)₄ was synthesized using hydrothermal techniques. It crystallizes in the monoclinic space group C2/m with the unit cell a=19.4317(10) Å, b=6.0249(3) Å, c=4.7788(2) Å, β=103.139(5)°. The crystal structure is an open framework having chains of edge sharing Co(1)O₆] octahedra. Other building blocks are TeO₃(OH)₂], PO₄] and Co(₂)O₂(OH)₄] connected mainly via corner sharing. The –OH groups protrude into channels in the structure. The magnetic susceptibility measured from 2 to 300 K shows two broad anomalies at around 21 K and 4 K, respectively. The peak at ∼20 K is ascribed to a two-dimensional antiferromagnetic ordering of linear Co(1)O₆] chains coupled by interchain interaction via PO₄] groups in the Co(1) sheets. The second transition at 4 K is ascribed to a second antiferromagnetic ordering of the moments of the Co(2) entities via super–super exchange involving PO₄] and TeO₃(OH)₂] groups. This assignment is strongly supported by low-temperature heat capacity measurements indicating an entropy removal within the high-temperature transition of about twice the magnitude of the low-temperature transition.