In situ XPS study of Pd(1 1 1) oxidation. Part 1: 2D oxide formation in 10 mbar O2

The oxidation of the Pd(1 1 1) surface was studied by in situ XPS during heating and cooling in 3 × 10⁻³ mbar O₂. A number of adsorbed/dissolved oxygen species were identified by in situ XPS, such as the two dimensional surface oxide (Pd₅O₄), the supersaturated O_ads layer, dissolved oxygen and the R 12.2° surface structure.Exposure of the Pd(1 1 1) single crystal to 3 × 10⁻³ mbar O₂ at 425 K led to formation of the 2D oxide phase, which was in equilibrium with a supersaturated O_ads layer. The supersaturated O_ads layer was characterized by the O 1s core level peak at 530.37 eV. The 2D oxide, Pd₅O₄, was characterized by two O 1s components at 528.92 eV and 529.52 eV and by two oxygen-induced Pd 3d_5/2 components at 335.5 eV and 336.24 eV. During heating in 3 × 10⁻³ mbar O₂ the supersaturated O_ads layer disappeared whereas the fraction of the surface covered with the 2D oxide grew. The surface was completely covered with the 2D oxide between 600 K and 655 K. Depth profiling by photon energy variation confirmed the surface nature of the 2D oxide. The 2D oxide decomposed completely above 717 K. Diffusion of oxygen in the palladium bulk occurred at these temperatures. A substantial oxygen signal assigned to the dissolved species was detected even at 923 K. The dissolved oxygen was characterised by the O 1s core level peak at 528.98 eV. The “bulk” nature of the dissolved oxygen species was verified by depth profiling.During cooling in 3 × 10⁻³ mbar O₂, the oxidised Pd²⁺ species appeared at 788 K whereas the 2D oxide decomposed at 717 K during heating. The surface oxidised states exhibited an inverse hysteresis. The oxidised palladium state observed during cooling was assigned to a new oxide phase, probably the R 12.2° structure.