Upconversion studies in Er doped TeO2-M2O (M=Li, Na and K) binary glasses

The luminescence properties of Er³⁺ doped alkali tellurite [ TeO₂-M₂O (M=Li, Na and K)] glasses are investigated. Infrared to visible upconversion emissions are observed at 410, 525, 550 and 658 nm using 797 nm excitation. These bands are assigned to the ²H_9/2  →⁴I_15/2, ²H_11/2  →⁴I_15/2, ⁴S_3/2  →⁴I_15/2, ⁴F_9/2  →⁴I_15/2 transitions of Er³⁺ respectively. Detailed study reveals that the ²H_9/2  →⁴I_15/2 transition at 410 nm involves a three-step process while the other transitions involve two-steps. Excitation with 532 nm radiation gives additional bands at 380, 404, 475 and 843 nm wavelengths due to the ⁴G_11/2  →⁴I_15/2, ²P_3/2  →⁴I_13/2, ²P_3/2  →⁴I_11/2, and ⁴S_3/2  →⁴I_13/2 transitions, respectively, along with the bands observed on NIR excitation. The fluorescence yield is found to be largest for the TeO₂-Na₂O glass. The lifetime of the ⁴S_3/2 level has been measured for all the three cases and used to explain the upconversion mechanisms. The fluorescence intensity ratio corresponding to the two thermally coupled levels (²H_11/2, ⁴S_3/2) has been used to estimate the temperature of the glass. It is observed that the temperature sensing capacity of TeO₂-Li₂O glass is better than the other two glasses.